With the main ingredient Nano titanium, high-grade multi-purpose waterproof titanium paint S500 is used to mix with cement. Under the principle of diffusion from the crystal technology ACC – American Crystalize Coating, the product prevents water from penetrating from the outside in order to be effectively waterproof – alkali resistant and maximize durability for cement surfaces as well as concrete structure.

Technical data:

-Ingredients: Titanium Dioxide, Membrane, mineral powder, active additives,…

-Surface drying time: 30 minutes

-Completely dry: 6-12 hours (average temperature 30°C humidity of the environment is about 80%)

-Number of paint layers: 2 coats

-Theoretical coverage: 10 – 13 m²/ liter/coat, depends on wall surface

 

Use

Surface preparation:

– All surfaces must be dry, free from dust, grease, lime, and old paint.

– New walls need to be dry for at least 25-30 days under normal conditions (average temperature ≥ 30°C, humidity of the environment is about ≤80%).

Construction:

– Prepare the mixture according to the following ratio: 1kg of water : 2 liters of cement : 4kg of S500.

– First, mix the cement and water thoroughly. Then mix the cement and water with a high-grade waterproofing agent. After mixing, the mixture must be used up within 1 hour, just mix as much as needed.

-Apply 2-3 coats by smooth roller, brush. Allow at least 6- 12 hours before recoating.

-It should be applied in good weather conditions don’t apply when the surface temperature is over 35°C and not less than 9°C.

-It is possible to cool the surface with a towel or a most roll, in case the dry weather can add a bit of water.

-Cleaning tools: Clean tools with water after use.

Store in a cool, dry, ventilated place. Place the paint can in a safe, upright position and close the lid tightly.

Health and save

No flammable, no lead, mercury, and other toxic substances should be safe for construction workers and users.

Note: The weight on the package may be with tolerance of ±2%

phone